Norme ASTM A967/A967M-17
Normes remplacées (1) ASTM A967/A967M-13. février 2013. Norme Annulée. Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. 1.1 This specification covers several different types of chemical passivation treatments for stainless steel parts. It includes recommendations and precautions for descaling, cleaning ...
A380/A380M Standard Practice for Cleaning
1.1 This practice covers recommendations and precautions for cleaning, descaling, and passivating of new stainless steel parts, assemblies, equipment, and installed systems. These recommendations are presented as procedures for guidance when it is recognized that for a particular service it is desired to remove surface contaminants that …
astm a 967 passivation
6.1 Passivation Treatment:6.1.1 Stainless steel parts shall be treated in one of the. following aqueous solutions and maintained within the speci-fied temperature range for the specified time. 6.1.1.1 Nitric 1—The solution shall contain 20 to 25 volumepercent of nitric acid and 2.5 6 0.5 weight percent of sodium.
ASTM A967 and AMS 2700 Standards for Passivation
ASTM A967. General industries use this standard to describe and control the passivation of stainless steel. Passivation is a process of making stainless steel more stainless than it would be if left alone. It is based on using an acid (nitric or citric) under highly controlled conditions to remove free iron particles from the surface and to help form a metal oxide …
ASTM A967 vs ASTM A380
ASTM A967 and ASTM A380 have similar mechanical properties. Both materials have a yield strength of 205 MPa and a tensile strength of 520 MPa. The main difference is that ASTM A967 has a higher elongation at break (10%) than ASTM A380 (8%). This means that ASTM A967 is more ductile than ASTM A380 and is better suited …
Corrosion of Stainless Steel: Test Methods and Proper Expectations
Per ASTM A967 and A380, stainless parts are shown to be properly passivated if they resist corrosion in salt spray for just 2 hours. Stainless steel performs relatively poorly in salt spray because the constant exposure to a harsh environment rapidly erodes the passivation layer and prevents it from reforming.
ASTM A967 vs ASTM A380
The main difference is that ASTM A967 has a higher elongation at break (10%) than ASTM A380 (8%). This means that ASTM A967 is more ductile than ASTM …
ASTM-A967 | Standard Specification for Chemical Passivation Treatments
The ASTM A967/A967-13 replaces ASTM A967/A967M-05 which is now obsolete. Keywords. cleaning of stainless steel; passivation; passivation tests; tests for cleanliness of stainless steels;; ICS Number Code 77.140.20 (Steels of high quality) To find similar documents by ASTM Volume: 01.03 (Steel--Plate, Sheet, Strip, Wire; Stainless Steel Bar)
ASTM A 967/A967M : 2017 | Chemical Passivation …
ASTM A 967/A967M : 2017. Current. Add to Watchlist. Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. Available format (s): Hardcopy, PDF. Language (s): English. Published date: 07-01-2017. Publisher: American Society for Testing and Materials.
Standard ASTM A967/A967M-17
ASTM A967/A967M-17. July 2017. Standard Current. Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. 1.1 This specification covers several …
A967 Standard Specification for Chemical
Scope. 1.1 This specification covers several different types of chemical passivation treatments for stainless steel parts. It includes recommendations and precautions for descaling, cleaning, and passivation of stainless steel parts. It includes …
ASTM
astm-a967, adoption notice: standardization specification for chemical passivation treatments for stainless steel parts (31-mar-1997) [superseding qq-p-35] astm-b26/b26m. astm-b26/b26m, adoption notice: aluminum alloy sand castings (15-may-1992) [superseding qq-a-601f] astm-d1000. 1994
Monitoring Passivation on Stainless Steel with Open …
Stainless Steel Parts, Equipment and Systems. ASTM A967 Standard provides tests with acceptance criteria to demonstrate that the passivation procedures have been successful. As per ASTM International Standards; "passivation testing is the process by which stainless steel will spontaneously form a chemically inactive surface when exposed to ...
ASTM A 380/A380M : 2017 | Stainless Steel Cleaning | SAI …
Fastener Part Standard - Hexagon Socket, Square Head, and Slotted Headless Set Screws - Inch Dimensioned. AWWA C220 : 2017. STAINLESS-STEEL PIPE, 1/2 IN. (13 MM) AND LARGER. ASTM A 781/A781M : 2018-02. SPECIFICATION FOR CASTINGS, STEEL AND ALLOY, COMMON REQUIREMENTS, FOR GENERAL …
ASTM A967/A967M-17
Full Description. 1.1 This specification covers several different types of chemical passivation treatments for stainless steel parts. It includes recommendations and precautions for descaling, cleaning, and passivation of stainless steel parts. It includes several alternative tests, with acceptance criteria, for confirmation of effectiveness of ...
WK84146 Revision of A967/A967M-17 Standard
Revision of A967/A967M-17 Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. Rationale. A967 was developed for replacement of Mil QQ-P 35. As part of the development, the word "dissolved" appears to be accidental dropped in para. 7.2. for the description of clean water. ... ASTM offers descriptions of …
NASA Corrosion Technology Laboratory (CTL) NASA …
Citric Acid Concentration: 4% ONLY in this phase. Immersion Times: 60, 90, and 120 minutes. Bath Temperatures: 38°C (100°F), 60°C (140°F), and 82°C (180°F) Salt Spray Testing per ASTM B 117. Corrosion Resistance Evaluation every 168 hours up to 504 hours of salt spray testing. Parameters resulting in the best corrosion resistance shall be ...
Standard Test Method for Compressive Strength of …
Scope. 1.1 This test method covers determination of compressive strength of cylindrical concrete specimens such as molded cylinders and drilled cores. It is limited to concrete having a density in excess of 800 kg/m 3 [50 lb/ft 3 ]. 1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard.
ASTM International
ASTM A967/A967M-17. July 1, 2017. Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. 1.1 This specification covers several …
ASTM A967 Passivation Standards | Able Electropolishing
The ASTM A967 passivation standard applies to the cleaning, passivation and testing of stainless steel parts. Chemical passivation removes free iron and other surface contaminants from stainless steel parts, improving corrosion resistance. Stainless steel passivation performed to the ASTM A967 standards meets these standards by passing …
WK77171 Revision of A967/A967M-17 Standard
Revision of A967/A967M-17 Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts. Rationale. ... ASTM Standard C33, 2003e1, "Specification for Concrete Aggregates," ASTM International, West Conshohocken, PA, 2003, DOI: 10.1520/C0033 ...
ASTM International
ASTM A967/A967M-17 July 1, 2017 Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts 1.1 This specification covers several different types of chemical passivation treatments for stainless steel parts. It includes recommendations and precautions for descaling, cleaning, and...
ASSIST-QuickSearch Document Details
Title: Chemical Passivation Treatments for Stainless Steel Parts (Replaced by ASTM-A967/A967M) Scope: This specification covers several different types of …
ASTM-A967 ADOPTION NOTICE STANDARDIZATION …
ASTM-A967, "Standardization Specification for Chemical Passivation Treatments for Stainless Steel Parts", was adopted on 31-MAR-97 for use by the Department of Defense (DoD). Proposed changes by DoD activities must be submitted to the DoD Adopting Activity: Defense Supply Center Richmond, Attn: DSCR-VFT/VEA, Richmond, VA 23297-5610.
What is ASTM A967?
1. Passivation Process: ASTM A967 defines the passivation process as the removal of free iron or other foreign matter from the surface of stainless steel by means of a chemical treatment. This treatment encourages the formation of a passive oxide layer, strengthening the steel's resistance to corrosion. 2.
Stainless Steel Passivation Services
Delstar is the industry leader in stainless steel passivation services, delivering the highest quality of passivated products to our customers since 2002. Here at Delstar Metal Finishing, we offer stainless steel passivation services with a focus on ASTM A967, ASTM A380, ASTM B912, and QQP35C specifications. Call or contact us today to speak to ...
Polishing & Passivation of Titanium -- ASTM A967
A. ASTM A967 [affil link] is often specified for passivation of titanium, although it is a misnomer for sure. What you are removing by "passivation" of titanium is any iron or iron oxide that may have been put on the surface in the fabrication process of the parts. Even though you do not truly passivate the titanium metal itself, you need to ...
(번역본)ASTM A967-01 Standard Specification for Chemical Passivation
ASTM A967-01 Standard Specification for Chemical Passivation Treatments for Stainless Steel Parts . 1. Scope(범위) * Stainless Steel 의 descaling, cleaning, passivation 에 대한 권고 및 예방책을 제시한다.
Understanding QQ-P-35: The Predecessor of ASTM A967 …
For example, ASTM A967 contains more options for passivation verification tests while AMS2700 provides more guidance on sampling large batches of components for testing and inspection after passivation. As the most direct linear descendant of QQ-P-35, AMS 2700 naturally shows its "heritage". QQ-P-35 types II, VI, VII and VIII are equivalent ...
Passivation | ASTM A967 | AMS 2700 | ASTM F86 | QQ-P-35 …
ASTM A967/A967M-17 (CITRIC ACID) 7.1.1.1 Citric 1—The solution shall contain 4 to 10 weight percent of citric acid. The parts shall be immersed for a minimum of 4 min at a temperature in the range from 60 to 70°C [140 to 160°F] 7.1.1.2 Citric 2—The solution shall contain 4 to 10 weight percent of citric acid.
Passivation Standards | Stellar Solutions
The following spec refers to ASTM A380 for passivation of stainless steel and thus allows the use of ASTM A967: MIL-DTL-14072D/E/F (Table IV. Finish E300) The spec MIL-T-704K in section 3.2.6 directly describes a passivation process analogous to QQ-P-35's type II followed by a chromate post-treatment. However, QQ-P-35 assigns this process as ...
ASTM A967/A967M-17
ASTM International [astm] PDF Price. $57.00. Add to cart Not a Member? Find out how to get ANSI Member Discount Others Also Bought. ASTM A380/A380M-17. Standard Practice for Cleaning, Descaling, and Passivation of Stainless Steel Parts, Equipment, and Systems ... ASTM A967/A967M-13; Included in Packages.